Binder jet 3D printing combined with post-deposition sintering is a non-beam additive manufacturing (AM) method for the creation of complex metallic structures. Binder saturation and particle morphology are two important factors affecting the quality of printed parts. Here, we investigated the effects of binder saturation on dimension accuracy, porosity, microstructure and microhardness of nickel-based alloy 625 samples made of differently atomized powders. Argon gas atomized (GA) and water atomized (WA) nickel-based alloy 625 powders were used to binder jet samples for a detailed comparative study. The optimal binder saturation for WA system is 60% to 70%, whereas for GA system the optimal is about 80%. Generally, GA samples achieved better overall quality than WA samples in terms of packing density, dimensional accuracy, sintered density, and microhardness. This difference is attributed mainly to the particle morphology including sphericity and roundness. The critical threshold for visible binder bleeding phenomenon in WA and GA systems is determined to be 120% and 140% binder saturation, respectively. Mechanisms for binder bleeding phenomenon at different saturation levels for WA and GA systems are discussed in detail. A pore evolution model is proposed to better understand the printing and sintering processes. 

Solidification or hot cracks are commonly observed defects in a number of metal alloys and may lead to deterioration of additively manufactured parts quality. In this study, ultra-high-speed x-ray radiography experiments enable the observation and characterization of bundles of hot-cracks that form in monobloc AA6061 substrate. The crack bundles are related to meltpool characteristics and pore formation. Crack propagation rate is also presented for the case of a crack that initiates from a pore. Two types of relevant pore formation are also described, namely keyhole porosity and crack-remelting porosity. The results of this study are expected to facilitate the validation of theoretical and numerical models of solidification cracking.